Effects of Initial Temperature and Tempering Medium on Thermal Tempering of Dental Porcelains
B. Hojjatie
Department of Dental Biomaterials, College of Dentistry, University of Florida, Gainesville, Florida 32610-0446
K.J. Anusavice
Department of Dental Biomaterials, College of Dentistry, University of Florida, Gainesville, Florida 32610-0446
The objective of this study was to test the hypothesis that quenching of porcelain in silicone oil rather than in compressed air will significantly increase the flexure strength by reducing the potential for crack formation during transient cooling. A secondary hypothesis to be tested is that the initial tempering temperature can be reduced significantly below the porcelain maturing temperature of 982°C but well above Tg without a decrease in strength. Opaque-body porcelain disks, 16 mm in diameter and 2 mm in thickness, with a thermal contraction mismatch (  ) of -1.5,0, and +3.2 ppm/°C were tempered from initial temperatures of 650, 750, 850, and 982°C in silicone oil with kinematic viscosities of 50,1000, and 5000 centistokes. Porcelain disks were also subjected to three cooling procedures in air: slow cooling in a furnace (SC), free convective cooling in a laboratory bench (FC), and tempering (T) by blasting the surface of body porcelain with air.
The crack size induced by a Vickers microhardness indenter was measured within one minute after crack development. For determination of the influence of initial cooling temperature on biaxial flexure strength, six body porcelain disks ( = 0) were tempered in air from initial temperatures of 650, 750, 850, and 982°C. The mean crack size of specimens tempered in oil was significantly smaller (p  0.001) than that of specimens that were slowly-cooled or fast-cooled in air for all thermal contraction mismatch cases. For the same initial temperature, the compatible system ( = 0) yielded a smaller crack size compared with the other mismatch levels. For specimens tempered in air, an increase in initial tempering temperature from 650°C to 850°C produced a 34% increase in flexure strength (80.2 MPa to 107.6 MPa). However, increasing the initial tempering temperature from 850°C to 982°C resulted in only a 7% increase in the mean flexure strength. The results of this study indicate that tempering of dental porcelains in air or in silicone oil from an initial temperature ranging from 650 to 850°C improved the resistance to crack initiation and failure. However, compared with oil quenching, tempering in air was associated with a smaller risk of thermal shock failure.
REFERENCES
- Anusavice KJ, DeHoff PH, Hojjatie B., Gray A. ( 1989). Influence of tempering and contraction mismatch on crack development in ceramic surfaces. J Dent Res 68:1182-1187.[Abstract/Free Full Text]
- Anusavice KJ, Hojjatie B. (1991). Effect of thermal tempering on strength and crack propagation of feldspathic porcelain. J Dent Res 70:1009-1013.[Abstract/Free Full Text]
- DeHoff PH, Anusavice KJ (1989). Tempering stresses in feldspathic porcelain. J Dent Res 68:134-138.[Abstract/Free Full Text]
- Gardon R. (1958). Calculation of temperature distributions in glass plates undergoing heat-treatment. JAm Ceram Soc 41:200-209.[CrossRef]
- Gardon R. ( 1980). Thermal tempering of glass. In: Uhlman DR, Kreidl NJ, editors. Glass science and technology. Vol. 5. New York (NY): Academic Press, 154.
- Gardon R. (1988). Tempering glass with modulated cooling schedules. JAm Ceram Soc 71:876-878.[CrossRef]
- Hojjatie B. (1990). Thermal tempering of layered ceramic structures (PhD dissertation). Gainesville (FL): University of Florida.
- Kirchner HP (1979). Strengthening of ceramics: treatments, tests, and design applications. New York (NY): Marcel Dekker, Inc., 35.
- Kirchner HP, Walker RE, Platts DR (1971). Strengthening alumina by quenching in various media. J Appl Phys 42:3685-3692.[CrossRef]
- Marshall DB (1980). An improved biaxial flexure test for ceramics. Ceramic Bull 59:551-553.
- Marshall DB, Lawn BR ( 1978). Measurement of nonuniform distribution of residual stresses in tempered glass disks. Glass Technol 19:57-58.
- Travitzky NA, Brandon DG, Gutmanas EY (1985). Effect of rapid cooling on the microstructure and mechanical properties of commercial 85 wt.% Al2O3. Mater Sci Eng 71:77-86.[CrossRef]
Journal of Dental Research, Vol. 72, No. 3,
566-571 (1993)
DOI: 10.1177/00220345930720030201
 CiteULike  Complore  Connotea  Del.icio.us  Digg  Reddit  Technorati  Twitter What's this?
This article has been cited by other articles:
|
|
|
|
 
I. L. Denry
Recent Advances in Ceramics for Dentistry
Critical Reviews in Oral Biology & Medicine,
January 1, 1996;
7(2):
134 - 143.
[Abstract]
[Full Text]
[PDF]
|
|
|
|
|