This Article Figures Only Full Text Full Text (PDF) Data Supplement Alert me when this article is cited Alert me if a correction is posted Citation Map Services Email this article to a friend Similar articles in this journal Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via Google Scholar Citing Articles via Scopus Google Scholar Articles by Shibata, Y. Articles by Swain, M.V. Search for Related Content PubMed Articles by Shibata, Y. Articles by Swain, M.V. Social Bookmarking                         What's this?

Micromechanical Property Recovery of Human Carious Dentin Achieved with Colloidal Nano-β-tricalcium Phosphate

¹ Department of Oral Biomaterials and Technology, Showa University School of Dentistry, 1-5-8 Hatanodai, Shinagawa-ku, Tokyo 142-8555, Japan; and
² Biomaterials Science Research Unit, Faculty of Dentistry, University of Sydney, Sydney Dental Hospital, Surry Hills, NSW 2010, Australia

Correspondence: ^* corresponding author, yookun{at}dent.showa-u.ac.jp

Reconstitution of carious dentin has been recognized as difficult, because it progresses by loss of collagen polymerization and by demineralization under acidic conditions. Recently, colloidal alkaline nano-calcium phosphate, prepared by electrical discharge in a buffered physiological saline solution, has been shown to be effective in the formulation of a bone-like biocomposite by simply being mixed with acidic collagen solution. It was hypothesized that colloidal calcium phosphate was suitable for the reconstitution of carious dentin. Natural caries lesions in dentin from permanent teeth were exposed to colloidal hydroxyapatite and β-tricalcium phosphate for 10 days. The micromechanical properties of these tissues were evaluated by nano-indentation. The elastic modulus of human carious dentin improved after samples were immersed in colloidal β-tricalcium phosphate. The mineral density of carious dentin exposed to β-tricalcium phosphate increased more than that immersed in hydroxyapatite. However, since it was not directly proportional to micromechanical recovery, mineral density alone was not a sufficient indicator of mechanical behavior.

Key Words: Nanoindentation • dentin • calcium phosphate • collagen

Journal of Dental Research, Vol. 87, No. 3, 233-237 (2008)
DOI: 10.1177/154405910808700315