This Article Free Full Text (Free PDF) Free References Alert me when this article is cited Alert me if a correction is posted Citation Map Services Email this article to a friend Similar articles in this journal Similar articles in PubMed Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via HighWire Citing Articles via Google Scholar Citing Articles via Scopus Google Scholar Articles by Xu, H.H.K. Search for Related Content PubMed PubMed Citation Articles by Xu, H.H.K. Social Bookmarking                         What's this?

Whisker-reinforced Heat-cured Dental Resin Composites: Effects of Filler Level and Heat-cure Temperature and Time

American Dental Association Health Foundation, Building 224, Room A-153, National Institute of Standards and Technology, 100 Bureau Dr. Stop 8546, Gaithersburg, MD 20899-8546; hockin.xu{at}nist.gov

Currently available dental resin composites are inadequate for use in large stress-bearing crown and multiple-unit restorations. The aim of this study was to reinforce heat-cured composites with ceramic whiskers. It was hypothesized that whiskers substantially strengthen heat-cured composites. It was further hypothesized that whisker filler level and heat-cure temperature and time significantly influence composite properties. Silica particles were fused onto the whiskers to facilitate silanization and to roughen the whiskers for improved retention in the matrix. The whisker filler mass fraction was varied from 0% to 79%, the heat-cure temperature from 80°C to 180°C, and cure time from 10 min to 24 hrs. Flexural strength, work-of-fracture, and fracture toughness of the composites were measured, and specimen fracture surfaces were examined with scanning electron microscopy. Filler level had a significant effect on composite properties. The whisker composite with 70% filler level had a flexural strength in MPa (mean ± SD; n = 6) of 248 ± 23, significantly higher than 120 ± 16 of an inlay/onlay composite control and 123 ± 21 of a prosthetic composite control (Tukey's multiple comparison test; family confidence coefficient = 0.95). Heat-cure time also played a significant role. At 120°C, the strength of composite cured for 10 min was 178 ± 17, lower than 236 ± 14 of composite cured for 3 hrs. The strength of whisker composite did not degrade after water-aging for 100 d. In conclusion, heat-cured composites were substantially reinforced with whiskers. The reinforcement mechanisms appeared to be whiskers bridging and resisting cracks. The strength and fracture toughness of whisker composite were nearly twice those of currently available inlay/onlay and prosthetic composites.

Key Words: ceramic whisker • filler level • heat cure • reinforcement mechanisms • resin composite • strength • toughness.

Journal of Dental Research, Vol. 79, No. 6, 1392-1397 (2000)
DOI: 10.1177/00220345000790060701


CiteULike    Complore    Connotea    Del.icio.us    Digg    Reddit    Technorati    Twitter    What's this?

This article has been cited by other articles:

				H. H.K. Xu, S. Takagi, L. Sun, L. Hussain, L. C. Chow, W. F. Guthrie, and J. H. Yen Development of a nonrigid, durable calcium phosphate cement for use in periodontal bone repair. J Am Dent Assoc, August 1, 2006; 137(8): 1131 - 1138. [Abstract] [Full Text] [PDF]

				D. Xie, I.-D. Chung, G. Wang, and J. Mays Synthesis and Evaluation of Novel Bifunctional Oligomer-based Composites for Dental Applications J Biomater Appl, January 1, 2006; 20(3): 221 - 236. [Abstract] [PDF]