This Article Full Text (PDF) References Alert me when this article is cited Alert me if a correction is posted Services Email this article to a friend Similar articles in this journal Similar articles in PubMed Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via Google Scholar Citing Articles via Scopus Google Scholar Articles by Van Loon, J.-P. Articles by De Bont, L.G.M. Search for Related Content PubMed PubMed Citation Articles by Van Loon, J.-P. Articles by De Bont, L.G.M. Social Bookmarking                         What's this?

Design and Wear Testing of a Temporomandibular Joint Prosthesis Articulation

'TMJ Research Group, Department of Oral & Maxillofacial Surgery, Groningen University Hospital, Groningen, The Netherlands

G.J. Verkerke

Department of Biomedical Engineering, University of Groningen, Groningen, The Netherlands

M.P. De Vries

Department of Biomedical Engineering, University of Groningen, Groningen, The Netherlands

L.G.M. De Bont

TMJ Research Group, Department of Oral & Maxillofacial Surgery, Groningen University Hospital, Groningen, The Netherlands

As part of the development of a total temporomandibular joint prosthesis, a prosthesis articulation was designed. The articulation consists of a spherical head (ball) of the mandibular part, rotating against an enveloping ultra-high-molecular-weight polyethylene (UHMWPE) disc with a flat cranial side, which slides along the opposing skull part. The aim of this study was to determine the in vitro wear rate of the articulation, and to predict the in vivo wear rate from the results. Based on a disc thickness of 5 mm and a ball diameter of 8 mm, the stresses within the disc were calculated by means of a finite element computer model. The wear rate of the ball-disc articulation was determined by in vitro wear tests, with a stainless-steel ball rotating against a UHMWPE disc in a serum-based lubricant. Eight discs were tested for seven million cycles each. The in vitro wear rate of the disc-skull part articulation was calculated from the test results of the ball-disc articulation. The maximum Von Mises' stress was less than the yield strength of UHMWPE and, therefore, was sufficiently low. The in vitro wear rate of the ball-disc articulation was 0.47 mm3 per million cycles. The in vivo expected total wear rate is 0.65 mm³ per year, corresponding with a yearly decrease of disc thickness of 0.0094 mm. Although it is difficult to judge whether this wear rate is sufficiently low, because the influence of UHMWPE wear particles in the TMJ region is unknown, both the expected wear rate and the decrease of thickness appear to be acceptable.

Key Words: temporomandibular joint • temporomandibular joint prosthesis • wear testing • prosthesis design • UHMWPE.

Journal of Dental Research, Vol. 79, No. 2, 715-721 (2000)
DOI: 10.1177/00220345000790020401