This Article Full Text (PDF) References Alert me when this article is cited Alert me if a correction is posted Citation Map Services Email this article to a friend Similar articles in this journal Similar articles in PubMed Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via Google Scholar Citing Articles via Scopus Google Scholar Articles by Xu, H.H.K. Search for Related Content PubMed PubMed Citation Articles by Xu, H.H.K. Social Bookmarking                         What's this?

Dental Composite Resins Containing Silica-fused Ceramic Single-crystalline Whiskers with Various Filler Levels

Paffenbarger Research Center, American Dental Association Health Foundation, National Institute of Standards and Technology, Building 224, Room A-153, Gaithersburg, Maryland 20899, USA

Currently available direct-filling composite resins are susceptible to fracture and hence are not recommended for use in large stress-bearing posterior restorations involving cusps. The glass fillers in composites provide only limited reinforcement because of the brittleness and low strength of glass. The aim of the present study was to use ceramic single-crystalline whiskers as fillers to reinforce composites, and to investigate the effect of whisker filler level on composite properties. Silica particles were fused onto the whiskers to facilitate silanization and to roughen the whiskers, thereby improving retention in the matrix. The composite flexural strength, elastic modulus, hardness, and degree of polymerization conversion were measured as a function of whisker filler mass fraction, which ranged from 0% to 70%. Selected composites were polished simulating clinical procedures, and the surface roughness was measured with profilometry. The whisker composite with a filler mass fraction of 55% had a flexural strength (mean ± SD; n = 6) of 196 ± 10 MPa, significantly higher than 83 ± 14 MPa of a microfill and 120 ± 16 MPa of a hybrid composite control (family confidence coefficient = 0.95; Tukey's multiple comparison). The composite modulus and hardness increased monotonically with filler level. The flexural strength first increased, then plateaued with increasing filler level. The degree of conversion decreased with increasing filler level. The whisker composite had a polished surface roughness similar to that of a conventional hybrid composite (p > 0.1; Student's t). To conclude, ceramic whisker reinforcement can significantly improve the mechanical properties of composite resins; the whisker filler level plays a key role in determining composite properties; and the reinforcement mechanisms appear to be crack pinning by whiskers and friction from whisker pullout resisting crack propagation.

Key Words: composite resin • reinforcement mechanism • strength • whisker filler level • polishability

Journal of Dental Research, Vol. 78, No. 7, 1304-1311 (1999)