This Article Full Text (PDF) References Alert me when this article is cited Alert me if a correction is posted Citation Map Services Email this article to a friend Similar articles in this journal Similar articles in PubMed Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via HighWire Citing Articles via Google Scholar Citing Articles via Scopus Google Scholar Articles by Mahler, D.B. Articles by Fleming, M.A. Search for Related Content PubMed PubMed Citation Articles by Mahler, D.B. Articles by Fleming, M.A. Social Bookmarking                         What's this?

Hg Emission from Dental Amalgam as Related to the Amount of Sn in the Ag-Hg (1) Phase

Oregon Health Sciences University, 611 SW Campus Drive, Portland, Oregon 97201

J.D. Adey

Oregon Health Sciences University, 611 SW Campus Drive, Portland, Oregon 97201

M.A. Fleming

Oregon Health Sciences University, 611 SW Campus Drive, Portland, Oregon 97201

Previous studies have shown that: (1) different dental amalgams emit different amounts of Hg vapor after surface films have been removed by abrasion (Boyer, 1988); (2) Sn oxide may be the predominant factor in these surface films that inhibit Hg vapor loss (Okabe et al., 1989); and (3) Sn in the Ag-Hg (₁) phase may influence the vapor pressure of ₁ (Reynolds, 1974). The purpose of this study was to explore the relationship between Hg vapor emission and the Sn content of the Ag-Hg (₁) phase in dental amalgam. Eleven commercial amalgams were selected whose ₁ phases contain different amounts of Sn. Amalgam specimens were ground on 600-grit carborundum paper and immediately placed into an apparatus designed around a gold film Hg vapor detector. Hg vapor loss in air over a 30-minute period was determined, and the log₁₀ Hg loss/volume fraction ₁ was plotted vs. the Sn content of the ₁ phase for the 11 test amalgams. A linear regression of these data, showing that of the higher the Sn content in ₁, the lower the Hg vapor loss, produced a highly significant R² = 0.94 (p < 0.001). To examine for differences in vapor pressure among alloys, we eliminated the oxidation effect by conducting these same tests in an argon atmosphere. Although the Hg loss was significantly greater in argon than in air, the same differences among alloys were observed. Thus, from the standpoint of both vapor pressure and oxidation, the amount of Sn in the ₁ phase of dental amalgam has a significant and specific influence on the potential for Hg vapor emission.

Key Words: Dental Amalgam • Mercury • Tin • Surface Properties • Spectrometry • X-ray Emission

Journal of Dental Research, Vol. 73, No. 10, 1663-1668 (1994)
DOI: 10.1177/00220345940730101201


CiteULike    Complore    Connotea    Del.icio.us    Digg    Reddit    Technorati    Twitter    What's this?

This article has been cited by other articles:

				M. Marek Dissolution of Mercury from Dental Amalgam at Different pH Values Journal of Dental Research, June 1, 1997; 76(6): 1308 - 1315. [Abstract] [PDF]

				H. Nakajima, Y. Akaiwa, H. Hashimoto, J.L. Ferracane, and T. Okabe Surface Characterization of Amalgam Made with Hg-In Liquid Alloy Journal of Dental Research, January 1, 1997; 76(1): 610 - 616. [Abstract] [PDF]

				J.L. Ferracane, J.D. Adey, H. Nakajima, and T. Okabe Mercury Vaporization from Amalgams with Varied Alloy Compositions Journal of Dental Research, July 1, 1995; 74(7): 1414 - 1417. [Abstract] [PDF]